| Trastomhas Nomina | Rp | HP | UHP | ||||
| Cumas iompair reatha | Dlús reatha | Cumas iompair reatha | Dlús reatha | Cumas iompair reatha | Dlús reatha | ||
| le linn | mm | A | A/cm2 | A | A/cm2 | A | A/cm2 |
| 12 | 300 | 10000-13000 | 14-18 | 13000-17400 | 17-24 | 15000-22000 | 20-30 |
| 14 | 350 | 13500-18000 | 14-18 | 17400-24000 | 17-24 | 20000-30000 | 20-30 |
| 16 | 400 | 18000-23500 | 14-18 | 21000-31000 | 16-24 | 25000-40000 | 19-30 |
| 18 | 450 | 22000-27000 | 13-17 | 25000-40000 | 15-24 | 32000-45000 | 19-27 |
| 20 | 500 | 25000-32000 | 13-16 | 30000-48000 | 15-24 | 38000-55000 | 18-27 |
| 22 | 550 | 32000-40000 | 13-16 | 35000-55000 | 14-22 | 42000-64000 | 17-26 |
| 24 | 600 | 35000-41000 | 13-15 | 41000-61000 | 14-21 | 50000-73000 | 17-25 |
| 28 | 700 | 39000-48000 | 10-12 | 55000-82000 | 14-21 | 67000-99000 | 17-25 |
| 32 | 800 | 43000-54000 | 8-10 | / | / | / | / |
Fáilte chun teagmháil a dhéanamh linn le haghaidh luachana.
Ríomhphost: info@zaferroalloy.com
Cad iad leictreoidí foirnéise stua leictreach ardchumhachta ardchumhachta (UHP), agus cén fáth a bhfuil siad ríthábhachtach maidir le déanamh cruach nua -aimseartha?
Ultra High Power (UHP) Electric Arc Furnace (EAF) electrodes are specialized graphite-based components designed to withstand extreme heat, electrical current, and chemical corrosion in EAFs-key equipment for melting scrap steel. Unlike conventional electrodes, UHP electrodes feature ultra-low resistivity (typically ≤10 μΩ·m), high mechanical strength (e.g., flexural strength >18 MPa), agus friotaíocht ocsaídiúcháin níos fearr. Laghdaíonn na hairíonna seo caillteanas fuinnimh le linn na hoibríochta, rud a chumasaíonn ionchur cumhachta níos airde (suas le 1000 kVa/tonna) agus rátaí leá níos tapúla. Tá siad ríthábhachtach do EAFanna scála {- scála (níos mó ná nó cothrom le 100 tonna) i muilte cruach nua -aimseartha, áit a spreagann éifeachtúlacht, táirgiúlacht, agus costais oibríochtúla laghdaithe éileamh. Cuireann leictreoidí UHP go díreach le tomhaltas leictreachais níos ísle (faoi ~ 15 {- 20% vs gráid chaighdeánacha) agus sconna níos giorra - go - amanna sconna, rud a fhágann go bhfuil siad fíor-riachtanach do tháirgeadh cruach ard-tréchur inbhuanaithe.